Ultrasonic joining of carbon-reinforced polyamide with oak wood for manufacturing sustainable hybrid structures
The feasibility of manufacturing strong and lightweight hybrid joints of carbon fiber-reinforced polyamide (PA6-15CF) and oak wood using ultrasonic energy was successfully demonstrated. Before joining, a groove pattern was generated on the surface of the wood plate by laser texturing. Wood platelets with and without texturing were joined with the polymer using the ultrasonic joining (U-Joining) process. Mechanical interlocking at the polymer-wood interface was improved, as the grooves and open vessels on the surface of the textured wood plate were filled with the polymer composite. Therefore, the lap-shear strength of joints with textured wood was 9.2 ± 0.7 MPa, whereas the shear strength of joints with untextured wood was just 4.1 ± 0.8 MPa.